Xm-12 15-5pH Precipitation Hardening Stainless Steel

• Type: Stainless Steel Bars
• Standard: ASTM
• Grade: High Quality Steel
• Certification: ISO
• Shape: Hot Rolled, Forged
• Technique: Round, Square, Flat
• Model NO.: XM-12
• Surface Treatment: Grinded, Peeled, Polished, Rough Turned
• Similar Grades: DIN 1.4545, Uns S15500, 15-5pH
• Size Range: Diameter: 20-480mm
• Delivery Condition: Annealed, Qunched and Tempered
• Surface Condition: Grinded, Peeled, Polished, Rough Turned
• Quality Standard: ASTM-A705
• Transport Package: Apply The Shipping Packing
• Specification: Diameter: 20-480mm
• Trademark: CHENGQUAN
• Origin: Hubei, Huangshi
• HS Code: 7228600000
• Production Capacity: 500tons Per Month

Product Description

Similar Grades:
DIN 1.4545, UNS S15500, 15-5PH
Shape:
Round, Flat, Square.
Size Range:

	Diameter(mm)	Thickness (mm)	Width (mm)	Length(mm)
Round	20-480	-	-	2000-5800
Square	20-480	-	-	2000-5800
flat	-	20-50	80-600	2000-5800

Steel-making Condition:
EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered

Surface Condition:
Black, Grinded, Peeled, Rough turned, Polished

Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
 

Packing details	In seaworthy packing, as your requirement.
Delivery details	within 30-50 days

Chemical Composition:

C	Mn	P	S	Si	Cr	Ni	Cu	Nb+Ta
0.07max	1.0max	0.030max	0.035max	1.0max	14.0-15.0	3.5-5.5	2.5-4.5	0.15-0.45

Mechanical Properties

Delivey Condition	Moduls of Elasticity(GPa)	Moduls of Rigidity(GPa)	Tensile Strength Rm (Mpa)	Yield Strength Rp0.2 (Mpa)	Elongation % in 2″ (50.8 mm)	Reduction Of Area (%)	Hardness (HRC)
A(annealed)	/	/	/	/	/	/	35 max
H 900	197.6	77.3	1378 min	1276 min	14 min	50min	44min
H925	/	/	1309 min	1207 min	14 min	54min	42min
H1025	/	75.9	1173 min	1138 min	15 min	56min	38min
H1075	/	69	1138 min	1035 min	16 min	58min	36min
H1100	/	/	1035 min	931 min	17 min	58min	34min
H1150	/	69	1000 min	862 min	19 min	60min	33min

Introduction:
15-5PH is a martensitic precipitation-hardening stainless steel that provides high strength, good
corrosion resistance, good mechanical properties at temperatures up to 600F (316C) and good toughness in both the longitudinal and transverse directions in both base metal and welds. Short-time, low-temperature heat treatments minimize distortion and scaling.
15-5PH is the ferrite-free version of 17-4PH Stainless Steel. Both alloys are widely used in the
aerospace, chemical, petrochemical, food processing, paper and general metalworking industries.


Applications:
Aircraft components
High pressure corrosive fabricated parts such as valves
Shafts
Fasteners
Fittings and gears