Hot Work Tool Steel, DIN 1.2365 Tool Steel Plate, DIN 1.2365 Steel Plate manufacturer / supplier in China, offering DIN 1.2365 Hot Work Tool Steel Plate, 1.3243 M35 Skh55 High Speed Steel, ASTM F1 Tool Steel with High Quality and so on.

(/ )

Supplier Homepage Product Mould Steel Hot Work Mould Steel DIN 1.2365 Hot Work Tool Steel Plate

DIN 1.2365 Hot Work Tool Steel Plate

FOB Price: US $1,500-5,500 / Ton
Min. Order: 1 Ton
Min. Order FOB Price
1 Ton US $1,500-5,500/ Ton
Get Latest Price
Production Capacity: 500tons Per Month
Transport Package: Seaworthy Packing
Payment Terms: L/C, T/T

Request a custom order and have something just for you!

Send Customized Request
Basic Info
  • Model NO.: DIN 1.2365
  • Standard: AISI, DIN
  • Surface Treatment: Black, Grinded, Machined, Rough Turned, Polished
  • Application: Container Plate
  • Stock: Stock
  • Quality Standard: BS En ISO 4957
  • Delivery Condition: Annealed, Quenched + Tempered
  • Trademark: Chengquan
  • Origin: Huangshi, China
  • Type: Steel Plate
  • Certification: ISO
  • Technique: Hot Rolled
  • Special Use: Wear Resistant Steel
  • Similar Grades: DIN 1.2365, H10
  • MOQ: 1t
  • Steel-Making Condition: Ef, Ef/Eaf+Lf+Vd, Ef/Eaf+ESR
  • Specification: DIN1.2365 H10
  • HS Code: 7228600000
Product Description
DIN 1.2365 H10 Hot Work Tool Steel

Similar Grade: DIN 1.2365, H10

Shape: Round, Flat, Square.

Size Range:
 Diameter(mm)Thickness (mm)Width (mm)Length(mm)
Round50-420--2000-5800
Square50-420--2000-5800
flat-20-5080-6002000-5800
 
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR

Delivery Condition:
Annealed , Quenched + Tempered

Surface Condition: 
Black, Grinded, Peeled, Rough turned, Polished

Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
 
Packing detailsIn seaworthy packing, as your requirement.
Delivery detailswithin 30-50 days
 
Chemical Composition:
GradeCSiMnPSCrMoV
1.23650.35-
0.45
0.80-
1.25
0.20-
0.70
0.030 max0.030 max3.00-
3.75
2.00-
3.00
0.25-
0.75
 
Heat Treatment:

FORGING: Heating for forging must be done slowly and uniformly. Soak through at 1900-2000°F, and reheat as often as necessary, stopping work when the temperature drops below 1650°F. After forging cool slowly in lime, mica, dry ashes or furnace. H10 hot work tool steel should always be annealed after forging.
 
ANNEALING: Heat slowly to 1550-1650°F, hold until the entire mass is heated through, and cool slowly in the furnace (40°F per hour) to about 1000°F, after which the cooling rate may be increased. Suitable precautions must be taken to prevent excessive carburization or decarburization.
 
SRAIN RELIEVING: stress reliving when desirable to relieve the strains of machining, heat slowly to 1050-1250°F, allow to equalize, and then cool in still air.
 
HARDENING: Warm slightly before charging into the preheat furnace, which should be operating at about 1400-1500°F. 1.2365 hot work tool steel is a very deep hardening steel, and although oil quenching may be used where maximum hardness is required, air hardening is recommended for most applications. The use of salt bath or controlled atmosphere furnace is desirable to minimize decarburization, and if not available, pack hardening spent pitch temperature employed Annealing is usually in the range of 1800-1900°F.
 
TEMPERING: Tempering practice may vary with size and application, but is usually performed in the temperature range of maximum secondary hardness or higher double tempering is recommended.

Applications:
Forging dies for steel, mandrels, dies, die holder bolsters and dummy blocks, punches, die inserts, gripper and header dies, hot shears, aluminum die casting dies.

Product Description:
1.2365 Chromium hot work tool steel has excellent resistance to softening at high temperatures. This particular grade is resisitant to thermal fatigue cracking and can be cooled in water for servicing.
 
 Contact Information:
FUSHUN SPECIAL STEEL CO., LTD.
 
Tel: 89-0731-89903933(CHANGSHA, Office)
Fax: +86-0731-89853933
Mobile : +86-15675829432
 
Website: www.fushunspecialsteel.com



 
 
 
 
Send your message to this supplier
Avatar
Mr. Crane
*From:
To: Mr. Crane
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

Find Similar Products By Category