BS En ISO 4957-DIN1.2367 Hot Work Tool Steel
|FOB Price:||US $1,700-5,500 / Ton|
|Min. Order:||1 Ton|
|Min. Order||FOB Price|
|1 Ton||US $1,700-5,500/ Ton|
|Production Capacity:||500tons Per Month|
|Transport Package:||Seaworthy Packing|
|Payment Terms:||L/C, T/T|
- Model NO.: DIN1.2367
- Standard: DIN, BS
- Surface Treatment: Black, Grinded, Rough Turned, Milled, Polished
- Application: Boiler Plate
- Stock: Stock
- Quality Standard: BS En ISO 4957
- Similar Grades: DIN1.2367, X38crmov5-3
- Specification: DIN1.2367, X38CrMoV5-3
- HS Code: 7228600000
- Type: Steel Plate
- Certification: ISO, SGS
- Technique: Forged, Rolled
- Special Use: High-strength Steel Plate
- Size Range: 20-780 mm
- Steel-Making Condition: Ef, Ef/Eaf+Lf+Vd, Ef/Eaf+ESR
- Trademark: Chengquan
- Origin: Huangshi, China
Similar Grade: DIN1.2367, X38CrMoV5-3
Shape: Round, Flat, Square.
|Diameter(mm)||Thickness (mm)||Width (mm)||Length(mm)|
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR
Annealed , Quenched + Tempered
Black, Grinded, Peeled, Rough turned, Polished
5.MOQ: 1 Ton
|Packing details||In seaworthy packing, as your requirement.|
|Delivery details||within 30-50 days|
|0.030 max||0.030 max||4.70-|
Chrome-molybdenum-vanadium steel for hardening in oil and in air with very good hardenability, high firmness during the heat and resistance to the tempering, very good toughness and plastic properties during normal and also higher temperatures.
Further the steel has a very good resistance to tearing of thermal fatigue and low sensitivity to quick changes of temperature. This hot work die steel is appropriate for the heat treatment also for firmness over 1800 N/mm2 and for tools cooled by water. It is well-workable during the heat and well-workable in the soft-annealed state. At request it can also be delivered in ESR quality.
Forging: Hot forming temperature: 1080-900ºC.
Soft annealing: Heat to 800-840ºC, cool slowly in furnace. This will produce a maximum Brinell hardness of 235.
Stress reliving: Stress relieving to remove machining stresses should be carried out by heating to 650ºC, holding for one hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening: Harden from a temperature of 1030-1080ºC followed by air, oil or warm bath (500-550ºC) quenching. Hardness after quenching is 53-57 HRC.
Wear resisting tools, pressure die casting tools, pressing tools for light and
heavy metal. For the highest requirements we recommend ESR or EFS quality.