DIN1.4923 Flat Stainless Steel with Superior Steel

• Type: Stainless Steel Flats
• Standard: DIN
• Grade: High Quality Steel
• Certification: ISO
• Shape: Flat
• Technique: Hot Rolled
• Model NO.: DIN1.4923
• Surface Treatment: Black, Grinded, Rough Turned, Peeled, Polished
• Size Range: 20-480 mm
• Steel-Making Condition: Steel-Making Condition: Ef, Ef/Eaf+Lf+Vd, Ef/Eaf+E
• Delivery Condition: Annealed, Quenched + Tempered
• MOQ: 1t
• Transport Package: Seaworthy Packing
• Specification: DIN1.4923
• Trademark: Chengquan
• Origin: Huangshi, China
• HS Code: 7228600000
• Production Capacity: 500tons Per Month

Product Description

Round Bar DIN1.4923 20Cr12Mo1V Stainless Steel

Similar Grade: DIN1.4923 20Cr12Mo1V 

Shape: Round, Flat, Square.

Size Range:
 

	Diameter(mm)	Thickness (mm)	Width (mm)	Length(mm)
Round	20-420	-	-	2000-5800
Square	20-420	-	-	2000-5800
flat	-	20-50	50-600	2000-5800

 
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR

Delivery Condition:
Annealed , Quenched + Tempered

Surface Condition: 
Black, Grinded, Peeled, Rough turned, Polished

Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
 
 

Packing details	In seaworthy packing, as your requirement.
Delivery details	within 30-50 days

 
Chemical Composition:
 

Grade	C	Mn	P	S	Si	Cr	Mo	Ni	V
1.4923	0.18- 0.24	0.30- 0.80	0.035 max	0.035 max	0.10- 0.50	11.0- 12.5	0.80- 1.20	0.30- 0.80	0.25- 0.35

 
 
 

Mechanical Properties(T=20°C if not differently stated)

Process	Diameter(mm)	Tensile Strength Rm (Mpa)	Yield Strength Rp0.2 (Mpa)	Elongation A5 (%)	Area Reduction Ratio C (%)	Hardness (HB)
Soft Annealing	/	/	/	/	/	255 max
Treated to hardness range	/	/	/	/	/	179-229
Treated to ferrite-pearlite structure	/	/	/	/	166-217
Quenched and tempered	11 max	1030-1320	835 min	9 min	40 min	/
Quenched and tempered	11-30	930-1230	785 min	10 min	45 min	/
Quenched and tempered	30-63	880-1180	735 min	10 min	45 min	/

 
 
 
 
Heat Treatment and Fabrication:
 
 

Process	Temperature(ºC)
End quench test Austenitizing	880 min
Carburizing	880-980
Core-hardening	840-880
Case-hardening	780-820
Tempering	150-200

 
 

Product Introduction:
Good machinability (hobbing and turning).
Good dimensional stability.
Homogenous PESR structure suitable for the production of large components.
Improved polishability, photo-etchability and EDM due to higher purity.
Suitable for single and double hardening.
 