DIN1.8519, 6150, BS970, En47, 735A50, 735A51 Spring Steels
|FOB Price:||US $500-5,000 / Ton|
|Min. Order:||1 Ton|
|Min. Order||FOB Price|
|1 Ton||US $500-5,000/ Ton|
|Production Capacity:||500tons Per Month|
|Transport Package:||Seaworthy Packing|
|Payment Terms:||L/C, T/T|
- Model NO.: DIN1.8519, 6150, BS970, EN47, 735A50, 735A51
- Standard: ASTM, GB, JIS, DIN
- Technique: Forged, Rolled
- Alloy: Alloy
- Size Range: 2-1000mm
- Quality Standard: DIN17222
- Trademark: Chengquan
- Origin: Huangshi, China
- Type: Spring Steel
- Steel Grade: High Quality Steel
- Surface Treatment: Black, Grinded, Peeled, Rough Turned, Polished
- Special Use: Fanster
- Similar Grades: DIN1.8519, 6150, BS970, En47, 735A50, 735A51
- MOQ: 1t
- Specification: 1.8519
- HS Code: 7228600000
Similar Grade: DIN1.8519, 6150, BS970, EN47, 735A50, 735A51
Shape: Round, Flat, Square.
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR
Cold Rolled only
Cold Rolled+Soft Annealed (G)
Cold Rolled+Soft Annealed+Cold Rolled (G+K)
Cold Rolled+Hardened+Tempered (H+A)
Grey Blue (GR)
Polished and Colour Tempered (P+AF)
5.MOQ: 1 Ton
|Packing details||In seaworthy packing, as your requirement.|
|Delivery details||within 20-50 days|
FORGING: Preheat carefully, then raise temperature to 1050°C for forging. Do not forge below 840°C. After forging cool slowly in a furnace.
ANNEALING: Heat slowly to 820-840°C, soak well and cool slowly in a furnace.
HARDENING: Heat slowly to 650-700°C and thoroughly soak. Continue to heat the 6150 steel to the final hardening temperature of 830-860°C and allow to be heated through. Oil quench.
TEMPERING: Temper 6150 spring steel immediately after hardening whilst tools are still hand warm. Re-heat to the tempering temperature then soak for one hour per 25 millimetre of total thickness (2 hours minimum) Cool in air. Tempering of this grade will be between 400-600°C for most applications.
Mill′s test certificate:
EN 10204/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing.
Spring Steels receive their special characteristics through quenching and tempering.
The processors need to make sure that their calculation method, design technique and processing procedure are aligned with the material. Precise temperature control is crucial for the part's characteristics.
Therefore, the temperature needs to be adjusted according to the respective purpose of the material.
Used widely in the motor vehicle industry AISI 6150 spring steels is suitable for many general engineering applications that require high tensile strength and toughness. Typical applications include crankshafts, steering knuckles, spindles, pumps and gears.