SAE 4137h Scm4h Steel with High Quality

• Type: Flat
• Standard: AISI, ASTM, JIS
• Composition: Ferrous Steel Scrap
• Technique: Hot Forged,or Hot Rolled
• Shape: Round,Flat or Square
• Surface Treatment: Black Surface, Grinded,Peeled,Milled,Polished
• Model NO.: SAE 4137H SCM4H 708M40
• Special Use: Alloy Structural Steel
• Application: Structural Steel Bar
• Size Range: Round Bar:Dia12~420mm Flat Bar:2~420 X 30~1500mm
• Smelting Process: Ef, Eaf, ESR
• Delivery Condition: Hot Rolled, Forged, Annealed,Quenched and Tempered
• Surface Condition: Black Surface, Grinded,Peeled,Milled,Polished
• Transport Package: Seaworth Packing
• Specification: Round Bar: Dia12~420mm Flat Bar: 2~420 X 30~1500mm
• Trademark: CHENGQUAN
• Origin: Huangshi, Hubei
• HS Code: 7228600000
• Production Capacity: 5000tons/Year

Product Description

Introduction:
SAE 4137H is an H-Steel gradeAlloy Steel. It is commonly called SAE 4137H Chromium-molybdenum steel.SAE 4137H offers good ductility and shock resisting properties combined with resistance to wear. With these characteristics it is a popular high tensile engineering steel with a tensile of 850-1000Mpa. At low temperatures it has reasonably good impact properties. It is also suitable for a variety of elevated temperature applications. For maximum wear and abrasion resistance the steel can be nitrided to give a shallow depth wear resistant case. Flame or induction hardening of 708M40T can give a case hardness of 50HRc or higher.
Applications:
SAE 4137H is now widely used in areas such as the motor, oil and gas industries. Suitable for components such as shafts, gears, spindles, bolts, studs and a wide variety of applications where a good quality high tensile steel grade is required.

All Grades Comparison

DIN	BS	SAE	ASTM	JIS	ANFOR	UNI	SS
1.7225	708M40	J1268	4137H	SCM4H	40CD4	38CrMo4KB	2244

Chemical Composition(%)

C	Mn	Si	P	S	Cr	Mo
0.34-0.41	0.60-1.00	0.15-0.35	0.035 max	0.040 max	0.75-1.20	0.15-0.25

Mechanical Properties(T=20°C if not differently stated)

Tensile Strength (Mpa)	Yield Strength(Mpa)	Fracture elongation A5 (%)	Notch impact energy ISO-V [J]	Hardness (HB)
850-1000	650 min	13 min	35 min	248-302

HEAT TREATMENT
Forging:Preheat SAE 4137H carefully, then raise temperature to 850-1200°C for forging. Do not forge below 850°C. After forging SAE 4137H, cool slowly in still air.
Annealing:Heat SAE 4137H slowly to 680-700°C. Cool in air.
Hardening:SAE 4137H is commonly supplied ready heat treated. If further heat treatment is required annealed SAE 4137H should be heated slowly to 860-890°C and after adequate soaking at this temperature quench in oil. Temper as soon as tools reach room temperature.