Uns S15500, DIN1.4545, Xm-12, 15-5pH Stainless Steel

• Type: Stainless Steel Flats
• Standard: ASTM, DIN, EN
• Certification: ISO
• Shape: Flat
• Similar Grades: Uns S15500, DIN1.4545, Xm-12, 15-5pH
• Steel-Making Condition: Ef, Ef/Eaf+Lf+Vd, Ef/Eaf+ESR
• Model NO.: UNS S15500, DIN1.4545
• Size Range: 10-800mm
• MOQ: 1t
• Transport Package: Seaworthy Packing
• Specification: UNS S15500, DIN1.4545
• Trademark: Chengquan
• Origin: Huangshi, China
• HS Code: 7228600000
• Production Capacity: 500tons Per Month

Product Description

DIN1.4545 Stainless Steel

Similar Grade: DIN1.4545, UNS S15500, XM-12, 15-5PH

Shape: Round, Flat, Square.

Size Range:
 

	Diameter(mm)	Thickness (mm)	Width (mm)	Length(mm)
Round	50-420	-	-	2000-5800
Square	50-420	-	-	2000-5800
flat	-	20-50	80-600	2000-5800

 
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR

Delivery Condition:
Annealed , Quenched + Tempered

Surface Condition: 
Black, Grinded, Peeled, Rough turned, Polished

Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
 
 

Packing details	In seaworthy packing, as your requirement.
Delivery details	within 30-50 days

 
Chemical Composition:
 

Grade	C	Mn	P	S	Si	Cr	Ni	Cu	Nb+Ta
1.4545	0.07 max	1.0 max	0.030 max	0.035 max	1.0 max	14.0- 15.0	3.5- 5.5	2.5- 4.5	0.15- 0.45

Heat Treatment and Mechanical Properties:
 

Delivery Condition	Modulus of Elasticity(GPa)	Modulus of Rigidity(GPa)	Tensile Strength Rm (Mpa)	Yield Strength Rp0.2 (Mpa)	Elongation % in 2″ (50.8 mm)	Reduction Of Area (%)	Hardness (HRC)
A(annealed)	/	/	/	/	/	/	35 max
H 900	197.6	77.3	1378 min	1276 min	14 min	50 min	44 min
H925	/	/	1309 min	1207 min	14 min	54 min	42 min
H1025	/	75.9	1173 min	1138 min	15 min	56 min	38 min
H1075	/	69	1138 min	1035 min	16 min	58 min	36 min
H1100	/	/	1035 min	931 min	17 min	58 min	34 min
H1150	/	69	1000 min	862 min	19 min	60 min	33 min

 
 

Applications:
Aircraft components
High pressure corrosive fabricated parts such as valves
Shafts
Fasteners
Fittings and gears
Product Description:
15-5PH is a martensitic precipitation-hardening stainless steel that provides high strength, good corrosion resistance, good mechanical properties at temperatures up to 600F (316oC) and good toughness in both the longitudinal and transverse directions in both base metal and welds. Short-time, low-temperature heat treatments minimize distortion and scaling.
1.4545 is the ferrite-free version of 17-4PH Stainless Steel. Both alloys are widely used in the aerospace, chemical, petrochemical, food processing, paper and general metalworking industries.