Hot Work Tool Steel, Tool Steel, Tool Steel Rod manufacturer / supplier in China, offering 1.2343, H11 Hot Work Tool Steel with High Quality, ASTM 201 Stainless Steel Round Bar with High Quality, Tool Steel Round Bar (O2, 90MnCrV8, 1.2842, BS BO2) and so on.

(/ )

Supplier Homepage Product Tool Steel Alloy Tool Steel 1.2343, H11 Hot Work Tool Steel with High Quality

1.2343, H11 Hot Work Tool Steel with High Quality

FOB Price: US $1,000-2,000 / Ton
Min. Order: 1 Ton
Min. Order FOB Price
1 Ton US $1,000-2,000/ Ton
Get Latest Price
Production Capacity: 500tons Per Month
Transport Package: Seaworthy Packing
Payment Terms: L/C, T/T, D/P

Request a custom order and have something just for you!

Send Customized Request
Basic Info
  • Model NO.: 1.2343
  • Standard: DIN
  • Technique: Forged, Rolled, Cold Drawn
  • Surface Treatment: Black, Grinded, Peeled, Rough Turned, Polished
  • Application: Tool Steel Bar
  • Surface Condition: Black, Grinded, Peeled, Rough Turned, Polished
  • Steel-Making Condition: Ef, Ef/Eaf+Lf+Vd, Ef/Eaf+ESR
  • Trademark: Chengquan
  • Origin: Huangshi, China
  • Type: Alloy Steel Bar
  • Composition: Ferrous Steel Scrap
  • Shape: Round, Flat, Square.
  • Special Use: Mold Steel
  • Size Range: 50-420mm
  • Delivery Condition: Annealed, Quenched + Tempered
  • Quality Standard: Ba En ISO 4957
  • Specification: 1.2343, H11
  • HS Code: 7228600000
Product Description
Similar Grade: 1.2343, H11.

Shape: Round, Flat, Square.

Size Range:
 Diameter(mm)Thickness (mm)Width (mm)Length(mm)
Round50-420--2000-5800
Square50-420--2000-5800
flat-20-5080-6002000-5800
 
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR

Delivery Condition: 
Annealed, Quenched + Tempered

Surface Condition: 
Black, Grinded, Peeled, Rough turned, Polished

Features:
1, Competitive price
2, Immediate delivery
3, Premium quality
4, Reliable service
Packing detailsIn seaworthy packing, as your requirement.
Delivery detailswithin 30-50 days
 
 
Chemical Composition:
GradeCMnPSSiCrVMo
1.23430.33-0.430.20-0.600.030
max
0.030
max
0.80-1.254.75-5.50.30-0.601.1-1.6

Mechanical Property:
UT: Material will be ultrasonically tested at appropriate stages of the manufacture to ensure the quality, as agreed between seller and purchaser.
 
Heat Treatment:
Hardness: Annealed(+A) max: 235 BHN
1.2343 tool steel when heat-treatment the preheat Temperature need reach 788°C, and the temperature may be ± 14 °C .
1.2343 tool steel when austenitizing, should keep 5-15 minutes long. If is the salt bath, temperature should keep in the 996 °C, and shall be ± 5.6 °C. Or is the controlled atmosphere furnaces, temperature should keep in the 1010 °C, and shall be ± 5.6 °C.
Quenching: 1.2343 tool steel Hardening quenching using air cooling, and it's hardness min is 53 RC. 
Tempering: 1.2343 tool steel general tempering temperature is 552°C. Double tempering of Double tempering of H11 tool steel is recommended.

Application:
1.2343/H11 tool steel are frequently used in cold work applications requiring toughness at relatively high hardness

Description:
1.2343/H11 tool steel is characterized by a controlled chromium content along with other alloying elements.
1.2343tool steel with excellent toughness.
1.2343 tool steel with high hardenability.
 Contact Information:
FUSHUN SPECIAL STEEL CO., LTD.
 
Tel: 89-0731-89903933(CHANGSHA, Office)
Fax: +86-0731-89853933
Mobile : +86-15675829432
 
Website: www.fushunspecialsteel.com

 
Send your message to this supplier
Avatar
Mr. Crane
*From:
To: Mr. Crane
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

Find Similar Products By Category