DIN1.3265, T5, Skh4 High Speed Steel

• Type: Alloy Steel Bar
• Standard: AISI, DIN, JIS, BS
• Composition: Ferrous Steel Scrap
• Technique: Forged
• Shape: Round, Flat
• Surface Treatment: Black, Grinded, Peeled, Rough Turned, Polished
• Model NO.: DIN 1.3265, T5, S18-1-2-10, SKH
• Special Use: High-strength Steel Plate
• Application: Tool Steel Bar
• Size Range: 10-420
• Quality Standard: BS En ISO 4957
• Steel-Making Condition: Ef, Ef/Eaf+Lf+Vd, Ef/Eaf+E
• Surface Condition: Black, Grinded, Peeled, Rough Turned, Polished
• MOQ: 1t
• Delivery Condition: Annealed, Quenched + Tempered
• Transport Package: Seaworthy Packing
• Specification: DIN 1.3265, T5, S18-1-2-10, SKH
• Trademark: FUSHUN
• Origin: Huangshi, China
• HS Code: 7228600000
• Production Capacity: 500tons Per Month

Product Description

DIN 1.3265, T5, S18-1-2-10, SKH4 High Speed Steel 

Similar Grade: DIN 1.3265, T5, S18-1-2-10, SKH4

Shape: Round, Flat, Square.

Size Range:

	Diameter(mm)	Thickness (mm)	Width (mm)	Length(mm)
Round	10-420	-	-	2000-5800
Square	-	1-300	-	2000-5800
flat	-	1-300	50-600	2000-5800

 
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR

Delivery Condition:
Annealed , Quenched + Tempered

Surface Condition: 
Black, Grinded, Peeled, Rough turned, Polished

Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
 

Packing details	In seaworthy packing, as your requirement.
Delivery details	within 30-50 days

 
Chemical Composition:

Grade	C	Mn	P	S	Si	Cr	Mo	W	V	Co
1.3265	0.72 -0.80	0.40 Max	0.45 Max	0.03 Max	0.03 Max	3.80- 4.50	0.50 -0.80	17.50- 18.50	1.40- 1.70	9.00- 10.00

 
Heat Treatment:
1. Preheat din 1.3265 steel slowly to the temperature of 820-870°C;
2. Heating up to quenching temperature of 1270-1290°C;
3. Make sure that the material is heated throughly;
4. Quench in the oil or brine;
5. Heat uniformly to the required tempering temperature;
6. Withdraw S18-1-2-10 steel from the furnace and cool in air;
7. The general tempering temperature is 540-560°C which makes the material 63HRC.
8. The 1.3265 tool steel is also suitable for vacuum hardening and triple tempering is strongly recommended.


Product Introduction:
High speed steel
 
 Contact Information:
FUSHUN SPECIAL STEEL CO., LTD.
 
  
 
   
 
Website: fushunmetal.en.made-in-china.com