Gold Member Since 2015
Audited Supplier
Huangshi Chengquan Metal Material Co., Ltd.

1018 Carbon Steel, 1018 Carbon Steel Bar, 1018 Steel manufacturer / supplier in China, offering AISI 1018 Carbon Steel with High Quality, AISI S1 Cold Work Steel with High Quality (DIN 1.2550), DIN1.2302 35CrMo7 Alloy Cold Work Tool Steel and so on.

(/ )

Supplier Homepage Product Structual Steel Carbon Structure Steel AISI 1018 Carbon Steel with High Quality

AISI 1018 Carbon Steel with High Quality

FOB Price: US $500-5,000 / Ton
Min. Order: 1 Ton
Min. Order FOB Price
1 Ton US $500-5,000/ Ton
Get Latest Price
Production Capacity: 500tons Per Month
Transport Package: Apply The Shipping Packing
Payment Terms: L/C, T/T

Request a custom order and have something just for you!

Send Customized Request
Basic Info
  • Model NO.: 1018
  • Standard: ASTM
  • Technique: Hot Rolled, Forged
  • Surface Treatment: Grinded, Peeled, Polished, Rough Turned
  • Application: Tool Steel Bar
  • Delivery Condition: Annealed, Qunched and Tempered
  • Quality Standard: ASTM-A29
  • Specification: Diameter: 20-480mm
  • HS Code: 7228600000
  • Type: Carbon Steel Bar
  • Composition: Ferrous Steel Scrap
  • Shape: Round, Square, Flat
  • Special Use: Mold Steel
  • Size Range: Diameter: 20-480mm
  • Surface Condition: Grinded, Peeled, Polished, Rough Turned
  • Trademark: CHENGQUAN
  • Origin: Hubei, Huangshi
Product Description
Shape: 
Round, Flat, Square.

Size Range:
 Diameter(mm)Thickness (mm)Width (mm)Length(mm)
Round20-480--2000-5800
Square20-480--2000-5800
flat-20-5080-6002000-5800
 
Steel-making Condition: 
EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered

Surface Condition: 
Black, Grinded, Peeled, Rough turned, Polished

Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
 
Packing detailsIn seaworthy packing, as your requirement.
Delivery detailswithin 30-50 days
 

Chemical Composition:

C
MnPSSiCrMoNi
0.15-0.200.60-0.900.040max0.050max////
 
 
Machining
The machinability of AISI 1018 mild/low carbon steel is graded at 78% of B1112.
 
Weldability
AISI 1018 mild/low carbon steel can be instantly welded by all the conventional welding processes. Welding is not recommended for AISI 1018 mild/low carbon steel when it is carbonitrided and carburized.
 
Low carbon welding electrodes are to be used in the welding procedure, and post-heating and pre-heating are not necessary. Pre-heating can be performed for sections over 50 mm. Post-weld stress relieving also has its own beneficial aspects like the pre-heating process.
 
Heat Treatment
The heat treatment for AISI 1018 mild/low carbon steel consists of the following processes:
 
Normalizing
AISI 1018 mild/low carbon steel should be heated at 890°C - 940°C and then cooled in still air.
Forging
This process requires heating between 1150°C - 1280°C and AISI 1018 mild/low carbon steel is held until the temperature becomes constant.
900°C is the minimum temperature required for the forging process.
The steel is then cooled in air after this process.
Tempering
AISI 1018 mild/low carbon steel is tempered at between 150°C - 200°C for improvement of case toughness. This process has little or no effect on hardness.
The occurrence of grinding cracks is reduced when AISI 1018 mild/low carbon steel is tempered at the above mentioned temperature.
Annealing
The AISI 1018 mild/low carbon steel is heated at 870°C - 910°C and allowed to cool in a furnace
Stress Relieving
500°C - 700°C is required to relieve stress in AISI 1018 mild/low carbon steel that is later cooled down in still air.
Case Hardening
This process requires heating to be carried out between 780°C - 820°C. AISI 1018 mild/low carbon steel is then quenched in water.
Core Refining
This is an optional process that requires heating at 880°C - 920°C.
AISI 1018 mild/low carbon steel after being heated is moistened in oil or water.
Carburizing
Carburizing takes place at 880°C - 920°C.
 
 
Applications 
It is used in bending, crimping and swaging processes.
Carburized parts that include worms, gears, pins, dowels, non-critical components of tool and die sets, tool holders, pinions, machine parts, ratchets, dowels and chain pins use AISI 1018 mild/low carbon steel.
It is widely used for fixtures, mounting plates and spacers.
It is suitably used in applications that do not need high strength of alloy steels and high carbon.
It provides high surface hardness and a soft core to parts that include worms, dogs, pins, liners, machinery parts, special bolts, ratchets, chain pins, oil tool slips, tie rods, anchor pins, studs etc.
It is used to improve drilling, machining, threading and punching processes.
It is used to prevent cracking in severe bends.

Introduction:
AISI 1018 mild/low carbon steel has excellent weldability and produces a uniform and harder case and it is considered as the best steel for carburized parts. AISI 1018 mild/low carbon steel offers a good balance of toughness, strength and ductility. Provided with higher mechanical properties, AISI 1018 hot rolled steel also includes improved machining characteristics and Brinell hardness.
Specific manufacturing controls are used for surface preparation, chemical composition, rolling and heating processes. All these processes develop a supreme quality product that are suited to fabrication processes such as welding, forging, drilling, machining, cold drawing and heat treating.
 
Contact Information:
FUSHUN SPECIAL STEEL CO., LTD.
Tel: 89-0731-89903933(CHANGSHA, Office)
Fax: +86-0731-89853933
Mobile: +86-18773142293
Website: www.fushunspecialsteel.com

Send your message to this supplier
Avatar
Mr. Crane
*From:
To: Mr. Crane
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now