DIN1.2210, 115CRV3, L2, Sks43 Alloy Steel

• Type: Carbon Steel Bar
• Standard: AISI, JIS, DIN
• Application: Structural Steel Bar
• Surface Treatment: Black, Grinded, Peeled, Rough Turned, Polished
• Alloy: Alloy
• Special Use: Cold Heading Steel
• Model NO.: DIN1.2210, 115CRV3, L2, SKS43
• Size Range: 12-300mm
• MOQ: 1t
• Steel-Making Condition: Ef, Ef/Eaf+Lf+Vd, Ef/Eaf+E
• Delivery Condition: Annealed, Quenched + Tempered
• Surface Condition: Black, Grinded, Peeled, Rough Turned, Polished
• Transport Package: Seaworthy Packing
• Specification: DIN1.2210, 115CRV3, L2, SKS43
• Trademark: FUSHUN
• Origin: Huangshi, China
• HS Code: 7228600000
• Production Capacity: 500tons Per Month

Product Description

DIN1.2210, 115CRV3, L2, SKS43 Alloy Steel

Similar Grade: DIN1.2210, 115CRV3, L2, SKS43 

Shape: Round, Flat, Square.

Size Range:

	Diameter(mm)	Thickness (mm)	Width (mm)	Length(mm)
Round	12-420	-	-	2000-5800
Square	12-420	-	-	2000-5800
flat	-	20-50	50-600	2000-5800

 
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered

Surface Condition: 
Black, Grinded, Peeled, Rough turned, Polished

Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
 

Packing details	In seaworthy packing, as your requirement.
Delivery details	within 30-50 days

 
Chemical Composition:

Grade	C	Mn	P	S	Si	Cr	Mo	V
1.2210	1.10- 1.25	0.20- 0.40	0.030	0.030	0.15- 0.30	0.50- 0.80	-	0.07- 0.12

 
Mechanical Properties:
Chromium-vanadium alloyed cold work tool steel with high wear resistance, high edge holding properties, simple heat treatment, good machinability and toughness properties, bright ground and polished according to standard DIN 670 h8.
Density: at 20 °C 7,80 kg/dm3 Thermal expansion between : 20 °C and... °C, 10-6 m/(mK)
Thermal conductivity: at 20 °C 32,0 W/(m.K)
 

100ºC	200ºC	300ºC	400ºC	500ºC
11.8	12.5	12.9	13.5	13.7

 

Heat Treatment:

Annealing: 710 - 750 °C

Hardness after annealing: Max. 220 HB

Stress relieving: Approx. 650 °C

Hot forming: 1050 - 850 °C

Hardening: 780 - 810 °C or 810 - 840 °C

Quenching media: 780 - 810 °C, Water 810 - 840 °C, Oil ( up to 15 mm diameter )

Hardness after quenching: 64 - 66 HRC
 

Applications:
Silver steel for guiding pins, small tools and structural parts in precision mechanics, button-type drills and jagged bits,
screw taps, milling cutters, broaching tools, piercing punches, ejector pins, twist drills, punches and taps, surgical instruments,
reamers, countersinks, dowels, engraving tools, metal cutting saws, axles and shafts, toothed drills, scraping
tools, gear cutters, mortice, wood chisels, guide rods.

Product Introduction:
Al-alloyed nitriding steel grade for large-sections.
 
Contact Information:
FUSHUN SPECIAL STEEL CO., LTD.
 
 
 
 
 

Website: fushunmetal.en.made-in-china.com