1.4429, AISI316ln, X2crnimon17-13-3 Austenitic Stainless Steel (EN1008-3)

• Type: Stainless Steel Bars
• Standard: AISI, DIN, EN
• Grade: High Quality Steel
• Certification: ISO
• Shape: Round, Flat, Square
• Technique: Forged, Rolled
• Model NO.: 1.4429, AISI316LN, X2CrNiMoN17-13-3
• Surface Treatment: Black, Grinded, Peeled, Rough Turned, Polished
• Size Range: 4-1000mm
• Similar Grades: 1.4429, AISI316ln, X2crnimon17-13-3
• Quality Standard: En10088
• MOQ: 1t
• Transport Package: Seaworthy Packing
• Specification: 1.4429, AISI316LN, X2CrNiMoN17-13-3
• Trademark: Chengquan
• Origin: Huangshi, China
• HS Code: 7228600000
• Production Capacity: 500tons Per Month

Product Description

1.4429, AISI316LN, X2CrNiMoN17-13-3 Austenitic Stainless Steel (EN1008-3)
Similar Grade:1.4429, AISI316LN, X2CrNiMoN17-13-3 
Shape: Round, Flat, Square.
Size Range:

Frame Processing    Shape	Round	Flat		Square
		Thickness	Width
Rolling	12-130mm	4-150mm	100-900mm	-
Forging	50-1000mm	70-800mm	300-2000mm	70-1000mm

 
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered

Surface Condition: 
Black, Grinded, Peeled, Rough turned, Polished

Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
 

Packing details	In seaworthy packing, as your requirement.
Delivery details	within 30-50 days

 
Chemical Composition:

Grade	C	Mn	P	S	Si	Cr	Ni	Mo
1.4429	0.030max	2.0 max	0.045 max	0.015 max	1.0 max	16.50- 18.50	11.0- 14.0	2.50- 3.00

 
 
Heat treatment:
Hardness: 250
Tensile strength: 580-800
Elongation after fracture: 40
Annealing Quench annealing should be performed at 1030 - 1110°C and followed by rapid cooling in water or air. For Ti-stabilised grades, annealing temperatures above 1070ºC may impair the resistance to intergranular corrosion. Ti-stabilised grades may also be given a stabilising treatment at lower temperatures. However, temperatures below 980°C should only be used after due consideration of the intended service environment. In applications where high residual stresses cannot be accepted, stress relief treatment may be necessary. This can be performed by annealing as outlined above, but may also be performed at lower temperatures. Please contact Outokumpu Stainless for further information. Hardening These grades cannot be hardened by heat treatment. However, they can be hardened by cold working.
Application:
Cutting tools
Drilling tools
 