DIN1.2825 95mnwcr5 Alloy Cold Work Tool Steel

• Type: Alloy Steel Bar
• Standard: DIN, BS
• Technique: Forged Rolled
• Application: Structural Steel Bar
• Surface Treatment: Black, Grinded, Peeled, Rough Turned, Polished
• Alloy: Alloy
• Model NO.: DIN1.2825 95MnwCr5
• Special Use: Mold Steel
• Similar Grades: DIN1.2825 95mnwcr5
• Size Range: 10-1000mm
• Quality Standard: BS En ISO 4957
• Steel-Making Condition: Ef, Ef/Eaf+Lf+Vd, Ef/Eaf+E
• Surface Condition: Black, Grinded, Peeled, Rough
• Transport Package: Seaworthy Packing
• Specification: DIN1.2825 95MnwCr5
• Trademark: FUSHUN
• Origin: China
• HS Code: 7228600000
• Production Capacity: 500tons Per Month

Product Description

DIN1.2825 95MnwCr5 Alloy Cold Work Tool Steel
Similar Grade: DIN1.2825, 95MnwCr5
Shape: Round, Flat, Square.
Size range:

Steel-making Shape	Round	Flat		Square
		Thickness	Width
Rolling	12-130mm	4-150mm	100-900mm	-
Forging	50-1000mm	70-800mm	300-2000mm	70-1000mm

 
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered

Surface Condition: 
Black, Grinded, Peeled, Rough turned, Polished

Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
 

Packing details	In seaworthy packing, as your requirement.
Delivery details	within 30-50 days

 
Chemical Composition:

Grade	C	Si	Mn	P	S	Cr	V	W
1.2825	0.90-1.00	0.10-0.40	1.05-1.35	0.030	0.030	0.40-0.65	0.05-0.20	0.40-0.70

 
Heat Treatment:
Forging: At 900° C-1100° C Cool slowly and anneal immediatedly
Annealing: At 880° C Cool slowly in furnace
Stress Relieving: At to 600° C-650° C Cool in still air
Hardening: Preheat at 600° C-850° C raise to 1020° C-1100° C Cool in air, iol or into salt bath held at 200° C-300° C and then air cool

Applications:
Cutting tools, Blanking and stamping dies , thread cutting tools, machine knivefor the wood paper and metal working industries, broaches, measuring tools, plastic moulds. 
Product Description:
> Low distortion.
> High wear resistance.
> Excellent polishability in hardened condition.
> High surface finish.
> Very low inclusion content.
> Low repair costs.
> Constant cycle times.