AISI D5 Tool Steel with High Quality (UNS T30405)

• Type: Alloy Steel Bar
• Standard: ASTM
• Composition: Ferrous Steel Scrap
• Technique: Hot Rolled, Forged
• Shape: Round, Square, Flat
• Surface Treatment: Grinded, Peeled, Polished, Rough Turned
• Model NO.: D5
• Special Use: Mold Steel
• Application: Tool Steel Bar
• Similar Grades: Uns T30405
• Size Range: Diameter: 20-480mm
• Quality Standard: ASTM-A681
• Delivery Condition: Annealed, Qunched and Tempered
• Surface Condition: Grinded, Peeled, Polished, Rough Turned
• Transport Package: Apply The Shipping Packing
• Specification: Diameter: 20-480mm
• Trademark: FUSHUN
• Origin: Hubei, Huangshi
• HS Code: 7228600000
• Production Capacity: 500tons Per Month

Product Description

Similar Grades:
UNS T30405
Shape:
Round, Flat, Square.
Size Range:
 

	Diameter(mm)	Thickness (mm)	Width (mm)	Length(mm)
Round	20-480	-	-	2000-5800
Square	20-480	-	-	2000-5800
flat	-	20-50	80-600	2000-5800

Steel-making Condition:
EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered

Surface Condition:
Black, Grinded, Peeled, Rough turned, Polished

Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton

 

Packing details	In seaworthy packing, as your requirement.
Delivery details	within 30-50 days

Chemical Composition(%)
 

C	Mn	P	S	Si	Cr	W	V	Mo	Co
1.4-1.60	0.10-0.60	<= 0.030	<=0.030	0.10-0.60	11.00-13.00	/	1.00max	0.70-1.20	2.50-3.50

Physical Properties
The physical properties of D5 tool steels are outlined in the following table:
 

Properties	Metric	Imperial
Density	7.7 - 8.03 x 1000 kg/m3	0.278 - 0.290 lb/in3
Melting point	1426°C	2600°F

Mechanical Properties
The mechanical properties of D5 tool steels are tabulated below.
 

Properties	Metric	Imperial
Poisson's ratio	0.27-0.30	0.27-0.30
Elastic modulus	190-210 GPa	27557-30457 ksi

Fabrication and Heat Treatment
Heat Treatment
D5 steels should be preheated very slowly up to 815°C (1500°F), then temperature should be increased to 1009°C (1850°F) and held for 20 to 45 minutes. Then they are air quenched.

Forging
Forging of D5 steels can be done at 1065°C (1950°F) down to 1750°F. Do not forge below 926°C (1700°F).

Annealing
Annealing of D5 steels should be done at 886°C (1627°F) followed by slow furnace cooling at 4°C (40°F) per hour or less.

Tempering
D5 steels can be tempered at 204°C (400°F) for achieving Rockwell C hardness of 61 and at 537°C (1000°F) for a Rockwell C hardness of 54.

Applications
Applications of D5 steels include thread rolling, blanking or forming dies operating at temperatures below 482°C (900°F).