High Speed Steel, DIN1.3247 High Speed Steel, DIN1.3247 Tool Steel manufacturer / supplier in China, offering DIN1.3247 M42 Skh59 High Speed Steel, 1.2825 Round Tool Steel Bar, SUS444 Steel Sheet with High Quality and Competitive Price and so on.

(/ )

Supplier Homepage Product Tool Steel High Speed Tool Steel DIN1.3247 M42 Skh59 High Speed Steel

DIN1.3247 M42 Skh59 High Speed Steel

FOB Price: US $1,500-6,800 / Ton
Min. Order: 1 Ton
Min. Order FOB Price
1 Ton US $1,500-6,800/ Ton
Get Latest Price
Production Capacity: 500tons Per Month
Transport Package: Seaworthy Packing
Payment Terms: L/C, T/T

Request a custom order and have something just for you!

Send Customized Request
Basic Info
  • Model NO.: DIN1.3247 M42 Skh59
  • Standard: ASTM, JIS, DIN
  • Technique: Hot Rolled
  • Special Use: High-strength Steel Plate
  • Similar Grades: DIN1.3247 M42 Skh59
  • Quality Standard: BS En ISO 4957
  • Trademark: Chengquan
  • Origin: Huangshi, China
  • Type: Steel Plate
  • Certification: ISO, SGS
  • Application: Ship Plate
  • Stock: Stock
  • Size Range: 10-620mm
  • Steel-Making Condition: Ef, Ef/Eaf+Lf+Vd, Ef/Eaf+ESR
  • Specification: DIN1.3247 M42 Skh59
  • HS Code: 7228600000
Product Description
1.3247 M42 SKH59 High speed Steel

Similar Grade: 1.3247, M42, SKH59

Shape: Round, Flat, Square.

Size Range:
 Diameter(mm)Thickness (mm)Width (mm)Length(mm)
Round2-200--2000-5800
Squarecontacted--2000-5800
flat-contactedcontacted2000-5800
 
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR

Delivery Condition:
Annealed , Quenched + Tempered

Surface Condition: 
Black, Grinded, Peeled, Rough turned, Polished

Characteristics:
1. All-round applicability
2. Good machine-ability
3. Good performance
4. Good hot hardness
5. Good wear resistance
 
 
Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
 
Packing detailsIn seaworthy packing, as your requirement.
Delivery detailswithin 30-50 days
 
Chemical Composition:
GradeCSiMnPSCrNiMoVWCoCu
DIN1.32471.05-
1.15
0.15-
0.40
0.15-0.400.030 max0.030 max3.50-4.250.3 max9.00-
10.00
0.95-
1.35
1.15-
1.85
7.75-
8.75
0.25 max



Heat Treatment:

Heat treatment temperatures, including rate of heating, cooling and soaking times will vary due to factors such as the shape and size of each M42 high speed steel component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities.
Hardness [HRc] 67, 69, 63

Forging: Pre heat the 1.3247 high speed steel slowly and uniformly to 650-760°C and equalise. Then increase more quickly to the forging temperature of 1010-1150°C and equalise prior to forging. Do not allow the forging temperature to drop below 980°C, if this occurs re heating will be necessary. Always cool the high speed steel very slowly after forging.

Annealing: Annealing of 1.3247high speed steel is recommended after hot working and before rehardening. Heat the 1.3247 high speed steel to 850°C at a rate of no more than 220°C per hour. Always hold at temperature for one hour per 25mm of thickness (with two hours being minimum). Furnace cool slowly. The 1.3247 high speed steel annealed hardness achieved should be 269 Brinell or lower.
Stress Relieving: If tools produced from 1.3247 high speed steel are heavily machined or ground it is recommended to stress relieve after machining and prior to hardening to minimise the possibility of distortion. To stress relieve heat the component to 600-650°C and soak well (approximately two hours) Cool slowly in the furnace. The 1.3247 high speed steel tools can be finish machined before heat treatment.

Hardening: For best results harden in a vacuum or controlled furnace, or in a properly rectified salt bath. Pre heat thoroughly in two steps to 450-500°C, then to 820-870°C, transfer to the high temperature salt bath or furnace. The exact hardening temperature to use for M35 will depend on the type of work being treated, but in general components should be hardened from the range of 1050-1250°C.

Tempering: For best results harden the 1.3247 high speed steel in a vacuum or controlled furnace, or in a properly rectified salt bath. Pre-heat the steel thoroughly to 820-870°C then transfer to the high temperature salt bath or furnace. The exact hardening temperature to use for 1.3247 high speed steel will depend on the type of work being treated, but in general components should be hardened from the range of 1160-1180°C in salt, or 1180-1190°C in atmosphere or vacuum furnaces. After a short hold at the hardening temperature, quench the component without further soaking into salt at 540-595°C or warm oil. If salt quenched allow the component to equalise at the bath temperature and then complete the quench in still air.

Temperature [°C] 500 550 600

Application:
DIN1.3247 high speed steel can be used in conditions where the demand for hot hardness is important. Commonly used for cutting tools including twist drills, taps, broaches tools, milling cutters, reamers, end mills, bandsaw blades, cold work tools, and thread rolling dies.

Description:
DIN1.33247 high speed steel is a premium cobalt high speed steel with a chemical composition designed for high hardness and superior hot hardness. These properties make the steel an excellent choice for machining high-strength and pre-hardened steels, high-hardness alloys, and the difficult-to-machine, nonferrous super alloys used in the aerospace, oil, and power generation industries.
DIN1.3247 high speed steel exhibits excellent wear resistance by virtue of high heat-treated hardness (68 to 70 HRC), and the high cobalt content imparts the hot hardness. As such, the cutting edges on tools made from 1.3247 high speed steel stay sharp and hard in heavy-duty and high-production cutting applications.
 
 Contact Information:
FUSHUN SPECIAL STEEL CO., LTD.
 
Tel: 89-0731-89903933(CHANGSHA, Office)
Fax: +86-0731-89853933
Mobile : +86-15675829432
 
Website: www.fushunspecialsteel.com
Send your message to this supplier
Avatar
Mr. Crane
*From:
To: Mr. Crane
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

Find Similar Products By Category