DIN1.7225 Alloy Steel, 708m40 Alloy Steel, Alloy Steel Bar manufacturer / supplier in China, offering DIN1.7225 708m40 Quenched and Tempered Alloy Steel, AISI S1 Cold Work Steel with High Quality (DIN 1.2550), DIN1.2302 35CrMo7 Alloy Cold Work Tool Steel and so on.

(/ )

Supplier Homepage Product Tool Steel Alloy Tool Steel DIN1.7225 708m40 Quenched and Tempered Alloy Steel

DIN1.7225 708m40 Quenched and Tempered Alloy Steel

FOB Price: US $500-3,000 / Ton
Min. Order: 1 Ton
Min. Order FOB Price
1 Ton US $500-3,000/ Ton
Get Latest Price
Production Capacity: 500tons Per Month
Transport Package: Seaworthy Packing
Payment Terms: L/C, T/T

Request a custom order and have something just for you!

Send Customized Request
Basic Info
  • Model NO.: DIN1.7225, SAE 4137H, SCM4H, 708M40
  • Standard: AISI, DIN, JIS
  • Technique: Hot Rolled
  • Surface Treatment: Black, Grinded, Peeled, Rough Turned, Polished
  • Application: Structural Steel Bar
  • Quality Standard: BS En ISO 4957
  • Steel-Making Condition: Ef, Ef/Eaf+Lf+Vd, Ef/Eaf+E
  • Trademark: Chengquan
  • Origin: Huangshi, China
  • Type: Alloy Steel Bar
  • Composition: Ferrous Steel Scrap
  • Shape: Round, Flat, Square.
  • Special Use: High-strength Steel Plate
  • Size Range: 50-420mm
  • MOQ: 1t
  • Delivery Condition: Annealed, Quenched + Tempered
  • Specification: 1.7225, SCM4H, 708M40
  • HS Code: 7228600000
Product Description
DIN1.7225 708M40 SAE4137H SCM4H Quenched and Tempered Alloy Steel

Similar Grade: DIN1.7225, SAE 4137H, SCM4H, 708M40

Shape: round, flat, square.

Size Range:

Diameter(mm)Thickness (mm)Width (mm)Length(mm)
Round50-420--2000-5800
Square50-420--2000-5800
flat-20-5080-6002000-5800
 
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR

Delivery Condition:
Annealed , Quenched + Tempered

Surface Condition: 
Black, Grinded, Peeled, Rough turned, Polished

Mechanical Properties:(T=20°C if not differently stated)

Tensile Strength (Mpa): 850-1000
Yield Strength(Mpa): 650 min
Fracture elongation A5 (%): 13 min
Notch impact energy ISO-V [J]: 35 min
Hardness (HB): 248-302
 
Features:
1. Competitive price
2. Immediate delivery
3. Premium quality
4. Reliable service
 
Packing detailsIn seaworthy packing, as your requirement.
Delivery detailswithin 30-50 days
 
Chemical Composition:
GradeCMnPSSiCrMo
1.72250.34-
0.41
0.60-
1.00
0.035 
max
0.040 
max
0.15-
0.35
0.75-
1.20
0.15-
0.25


Heat Treatment:
Forging: Preheat 1.7225 carefully, then raise temperature to 850-1200ºCfor forging. Do not forge below 850ºC. After forging 1.7225, cool slowly in still air.
Annealing: Heat SAE 4137H slowly to 680-700ºC. Cool in air.
Hardening:SAE 4137H is commonly supplied ready heat treated. If further heat treatment is required annealed 1.7225 should be heated slowly to 860-890ºC and after adequate soaking at this temperature quench in oil. Temper as soon as tools reach room temperature.
Tempering: Heat the component carefully to a suitable temperature selected by reference to a tempering chart or table, soak at the temperature for two hours per 25mm of ruling section, then allow to cool in air. Tempering between 250-375ºC is not advised as tempering within this range will seriously reduce the impact value.

Application:
1.7225 is now widely used in areas such as the motor, oil and gas industries. Suitable for components such as shafts, gears, spindles, bolts, studs and a wide variety of applications where a good quality high tensile steel grade is required.
 
Product Description:
1.7225 is an H-Steel grade Alloy Steel. It is commonly called 1.7225 Chromium-molybdenum steel. 1.7225 offers good ductility and shock resisting properties combined with resistance to wear. With these characteristics it is a popular high tensile engineering steel with a tensile of 850-1000Mpa. At low temperatures it has reasonably good impact properties. It is also suitable for a variety of elevated temperature applications. For maximum wear and abrasion resistance the steel can be nitrided to give a shallow depth wear resistant case. Flame or induction hardening of 708M40T can give a case hardness of 50HRc or higher.

Contact Information:
FUSHUN SPECIAL STEEL CO., LTD.
Tel: 89-0731-89903933(CHANGSHA, Office)
Fax: +86-0731-89853933
Mobile: +86-15675829432
 

Website: www.fushunspecialsteel.com
 
 
Send your message to this supplier
Avatar
Mr. Crane
*From:
To: Mr. Crane
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

Find Similar Products By Category