High Speed Tool Steel 1.3343

• Type: HSS
• Standard: AISI, ASTM, DIN, JIS
• Technique: Rolled , Forged
• Shape: Round
• Surface Treatment: Black, Grinded, Peeled, Rough Turned, Polished
• Special Use: Mold Steel
• Model NO.: M2 / Skh51 / 1.3343 / W6Mo5Cr4V
• Application: Tool Steel Bar
• Size Range: 50-420mm
• Delivery Condition: Annealed, Quenched+Tempered
• Surface Condition: Black, Grinded, Peeled, Rough Turned, Polished
• MOQ: 1t
• Similar Grades: 1.3343 / Skh51 / M2 / W6mo5cr4V2
• Transport Package: Seaworthy Packing
• Specification: 1.3343
• Trademark: FUSHUN
• Origin: Huangshi
• HS Code: 7228600000
• Production Capacity: 500tons Per Month

Product Description

Similar Grades:1.3343 / Skh51 / M2 / W6Mo5Cr4V2
Shape: round, flat, square.
Size Range:

	Diameter(mm)	Thickness (mm)	Width (mm)	Length(mm)
Round	50-420	-	-	2000-5800
Square	50-420	-	-	2000-5800
flat	-	20-50	80-600	2000-5800

 
Delivery Condition:
 Annealed, Quenched+Tempered
Surface Condition: 
Black, Grinded, Peeled, Rough turned, Polished,
Features:  
1. Immediate delivery
2. Premium quality
3. Reliable service
 

Packing details	In seaworthy packing, as your requirement.
Delivery details	within 30-50 days

Chemical Composition(%):

Steel Grade	C	Mn	Si	Cr	Mo	V	W
M2	0.78-0.88	0.15-0.40	0.45 max	3.75-4.50	4.5-5.5	1.75-2.2	5.5-6.75

 
Heat Treatment:
Preheat at 1450 F before heating for hardening. Then heat rapidly from 1450 F to 2200 F and hold for 3 to 5 minutes followed by quenching in oil, air or salt bath.

Application:  
Typical applications for 1.3343 high speed steel are twist drills, reamers, broaching tools, taps, milling tools, metal saws. M2 high speed steel is suitable for cold forming tools such as extrusion rams and dies, also cutting tools, plastic moulds with elevated wear resistance and screws .