20mnmoni4-5 1.6311 Special Steel for Boiler and Pressure Vessel

• Type: Flat
• Standard: DIN
• Composition: Ferrous Steel Scrap
• Technique: Hot Forged,or Hot Rolled
• Shape: Round,Flat or Square
• Surface Treatment: Polished,Grinded or Peeled
• Model NO.: 20MnMoNi4-5 1.6311
• Special Use: Alloy Structural Steel
• Application: Structural Steel Bar
• Transport Package: Seaworth Packing
• Specification: Round Bar: Dia12~420mm Flat Bar: 2~420 X 30~1500mm
• Trademark: CHENGQUAN
• Origin: Huangshi, Hubei
• HS Code: 7228100000
• Production Capacity: 5000tons/Year

Product Description

Applications• Boiler installations in accordance with Technical Rules TRD 101, EN 12952 etc. for temperatures up to 375 °C.
• Pressure vessel installations in accordance with the AD 2000-Merkblätter series W and HP for temperatures of - 10 °C to 375 °C.All Grades Comparison

DIN	EN
1.6311	20MnMoNi4-5

Quality StandardEN 10250 Open steel die forgings for general engineering purposes. Alloy special steelsChemical Composition(%)

C	Mn	Si	P	S	Cr	Ni	Mo
0.17-0.23	1.00-1.50	0.40 max	0.035 max	0.035 max	0.50 max	0.40-0.80	0.45-0.60

Mechanical Properties(T=20°C if not differently stated)

Process	Diameter(mm)	Tensile Strength Rm (Mpa)	Yield Strength Rp0.2 (Mpa)	Elongation A5 (%)	Impact Value Kv (J) Room Temperature
QUENCHED AND TEMPERED	40 max	590-750	470 min	18 min	35 min
QUENCHED AND TEMPERED	40-60	590-730	460 min	18 min	35 min
QUENCHED AND TEMPERED	60-100	570-710	450 min	18 min	35 min
QUENCHED AND TEMPERED	100-160	570-710	440 min	18 min	35 min
QUENCHED AND TEMPERED	160-330	550 min	390 min	17 min	39 min

HEAT TREATMENT:

1. Stress Relieving: Heat to 580 - 620°C. Generally the maximum stress relieving time shall be restricted to 150 min. If it exceeds 90 min or in case of repeated heat treatment the lower range of recommended temperatures shall apply.Austenitizing + Quenchingg: Heat to 870 to 940 °C. After temperature achievement over the whole section cooling in waterTempering: Heat to 610 to 690 °C. Holding 30 min time after temperature achievement over the whole section, cooling in still air

Forming properties and weldability:1.6311 Special Steel can be hot or cold formed and can be welded and flame cut according to the general procedures. The guidelines
according to EN 1011 and VdTÜV-material data sheet 440/1 shall be observed. For the fabrication of pressure vessels in accordance with AD 2000 Merkblatt in the context of PED qualified welding consumables have to be applied.Mill′s test certificate:EN 10204/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing.