DIN1.2661 SKD8 38crcowv18-17-17 Alloy Hot Work Tool Steel

• Type: Alloy Steel Bar
• Standard: JIS, DIN, BS
• Technique: Forged, Rolled
• Application: Tool Steel Bar
• Surface Treatment: Black, Grinded, Peeled, Rough Turned, Polished
• Alloy: Alloy
• Model NO.: DIN1.2661 SKD8 38CrCoWV18-17-17
• Special Use: Mold Steel
• Similar Grades: DIN1.2661 SKD8 38crcowv18-17-17
• Size Range: 10-800mm
• Quality Standard: BS En ISO 4957
• Delivery Condition: Annealed, Quenched + Tempered
• Transport Package: Seaworthy Packing
• Specification: DIN1.2661 SKD8 38CrCoWV18-17-17
• Trademark: FUSHUN
• Origin: China
• HS Code: 7228600000
• Production Capacity: 500tons Per Month

Product Description

DIN1.2661 SKD8 38CrCoWV18-17-17 Alloy Hot Work Tool Steel

Similar Grade: DIN1.2661, SKD8, 38CrCoWV18-17-17

Shape: Round, Flat, Square.

Size range:

Steel-making Shape	Round	Flat		Square
		Thickness	Width
Rolling	12-130mm	4-150mm	100-900mm	-
Forging	50-1000mm	70-800mm	300-2000mm	70-1000mm

 
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered

Surface Condition: 
Black, Grinded, Peeled, Rough turned, Polished

Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
 

Packing details	In seaworthy packing, as your requirement.
Delivery details	within 30-50 days

 Chemical Composition:

Grade	C	Si	Mn	P	S	Cr	Mo	V	W
1.2661	0.35- 0.45	0.15- 0.50	0.20- 0.50	0.030 max	0.030 max	4.00- 4.70	0.30-0.50	1.70-2.10	3.80-4.50

 
Heat Treatment:
Hardness(Annealed): 260HB
Hardening temperature: 1120ºC
Quenching medium: oil
Tempering temperature: 600ºC
Hardness HRC: 48
 
Mechnical Property:

UT Class

According to Standard of SEP 1921/84,100% Volume, Level C/c, D/d or E/e

 

Applications:
Cutting tools, Blanking and stamping dies , thread cutting tools, machine knivefor the wood paper and metal working industries, broaches, measuring tools, plastic moulds. 
Product Description:
> Low distortion.
> High wear resistance.
> Excellent polishability in hardened condition.
> High surface finish.
> Very low inclusion content.
> Low repair costs.
> Constant cycle times.