Similar grades: H10, SKD7, 32CrMoV12-28
Shape: Round, Flat, Square, Sheet
Size range:
Round bar:
Diameter : 1mm-2000mm
Square bar:
Size: 50mm * 50mm-600mm *600mm
flat bar:
Size: Thickness: 0.1mm-800mm Width: 10mm to 1500mm
pipe:
Size: OD: 6-219mm WT: 1-35 mm.
Cold-rolled sheet:
Thickness: 2-5mm Width:1000mm Length: 2000mm
Hot-rolled sheet:
Thickness:6-80mm Width: 210-610mm
Length: We can supply any length based on the customer's requirement.
Delivery condition:Annealed, Qunched and Tempered
Surface conditions: Grinded\Peeled (Centreless Turned)\Polished\Ground
Features:1:Competitive price
2 Immediate delivery
3.Premium quality
4.Reliable service
Chemical Composition:
| |
C |
Si |
Mn |
P |
S |
Cr |
V |
Mo |
| Min% |
0.28 |
0.10 |
0.15 |
|
|
2.70 |
0.40 |
2.50 |
| Max% |
0.35 |
0.40 |
0.45 |
0.025 |
0.005 |
3.20 |
3.00 |
0.70 |
Properties :
Hot work tool steel with high resistance to thermal shocks and fatigue, good thermal conductivity, hot tensile and impact
strength, resistance to tempering, fine grain size with high toughness, extra fine structure without grain boundary
carbide, high creep strength at elevated temperature, insensitive to constant temperature change, low P and S content,
suitable for water cooling. This grade can be produced on request by the process EFS, ESR or VAR.
Furnaces for metallurgical processing:
electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirement.
Applications :
Highly stressed hot work tools in die forging presses for steels, brass and non ferrous metals, pressure casting dies for
heavy and light metal alloys, mandrels, inner liners, stems, die holders, dummy blocks, pressure pads, bolsters, dies and
containers for metal tube and rod extrusion, hot extrusion tools, single block inserts and dies for presses, tools for the
manufacture of hollows, screws, nuts, bolts and rivets, hot shear blades, forging dies and press die inserts, die casting
tools, hot forming dies, hot gripper and header dies.
Physical Properties :
Density : at 20 °C 7,85 kg/dm3
Thermal expansion between : 20 °C and... °C, 10-6 m/(mK)
Thermal conductivity : at 20 °C 30,0 W/(m.K)
| 100ºC |
200ºC |
300ºC |
400ºC |
500ºC |
| 12.0 |
12.5 |
12.7 |
13.0 |
13.2 |
Heat Treatment :
Annealing : 750 - 800 °C
Hardness after annealing : Max. 205 HB
Stress relieving : 600 - 650 °C
Hot forming : 1100 - 900 °C
Hardening : 1010 - 1050 °C
Quenching media : Oil, Salt bath ( 500 - 550 °C )
Hardness after quenching : 52 - 56 HRC
Hardness after tempering :
| 400ºC |
500ºC |
550ºC |
600ºC |
| 500HRC |
51HRC |
52HRC |
50HRC |