DIN 1.5752 AMS 6260e 655h13 15nicr13 Case Hardening Steel Bar

• Type: Round
• Standard: AISI, DIN, BS
• Composition: Ferrous Steel Scrap
• Technique: Forged
• Shape: Round Flat
• Surface Treatment: Black, Grinded, Peeled, Rough Turned, Polished
• Model NO.: DIN1.5752 AMS6260E 655H13 15NiCr13
• Special Use: Mold Steel
• Application: Structural Steel Bar
• Size Range: 20-480 mm
• Quality Standard: BS En 10084 2008
• MOQ: 1t
• Steel-Making Condition: Ef, Ef/Eaf+Lf+Vd, Ef/Eaf+E
• Transport Package: Seaworthy Packing
• Specification: DIN1.5752 AMS6260E 655H13 15NiCr13
• Trademark: FUSHUN
• Origin: , China
• HS Code: 7228600000
• Production Capacity: 500tons Per Month

Product Description

DIN1.5752 AMS6260E 655H13 15NiCr13 Case Hardening Steel

Similar Grade: DIN1.5752 AMS6260E 655H13 15NiCr13 

Shape: Round, Flat, Square.

Size Range:

	Diameter(mm)	Thickness (mm)	Width (mm)	Length(mm)
Round	20-420	-	-	2000-5800
Square	20-420	-	-	2000-5800
flat	-	20-50	50-600	2000-5800

 
Steel-making Condition: EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered

Surface Condition: 
Black, Grinded, Peeled, Rough turned, Polished

Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
 

Packing details	In seaworthy packing, as your requirement.
Delivery details	within 30-50 days

 
Chemical Composition:

Grade	C	Mn	P	S	Si	Cr	Ni
1.5752	0.14- 0.20	0.40- 0.70	0.025 max	0.035 max	0.40 max	0.60- 0.90	3.00- 3.50

 
 
 

Mechanical Properties(T=20°C if not differently stated)

Process	Diameter(mm)	Tensile Strength Rm (Mpa)	Yield Strength Rp0.2 (Mpa)	Elongation A5 (%)	Area Reduction Ratio C (%)	Hardness (HB)
Soft Annealing	/	/	/	/	/	255 max
Treated to hardness range	/	/	/	/	/	179-229
Treated to ferrite-pearlite structure	/	/	/	/	166-217
Quenched and tempered	11 max	1030-1320	835 min	9 min	40 min	/
Quenched and tempered	11-30	930-1230	785 min	10 min	45 min	/
Quenched and tempered	30-63	880-1180	735 min	10 min	45 min	/

 
 
 
 
Heat Treatment and Fabrication:
 

Process	Temperature(ºC)
End quench test Austenitizing	880 min
Carburizing	880-980
Core-hardening	840-880
Case-hardening	780-820
Tempering	150-200

 
 

Product Introduction:
Good machinability (hobbing and turning).
Good dimensional stability.
Homogenous PESR structure suitable for the production of large components.
Improved polishability, photo-etchability and EDM due to higher purity.
Suitable for single and double hardening.
 
 Contact Information:
FUSHUN SPECIAL STEEL CO., LTD.
 
  
 
   
 
Website: fushunmetal.en.made-in-china.com