Cold Drawn 304 Stainless Steel Flat Bar with High Quality

• Type: Stainless Steel Flats
• Standard: ASTM
• Grade: High Quality Steel
• Certification: ISO
• Shape: Round, Square, Flat
• Technique: Hot Rolled, Forged
• Model NO.: 304
• Surface Treatment: Grinded, Peeled, Polished, Rough Turned
• Similar Grades: SUS 304
• Size Range: 3mm*10mm-30mm*180mm.
• Delivery Condition: Annealed, Qunched and Tempered
• Surface Condition: Grinded, Peeled, Polished, Rough Turned
• Quality Standard: ASTM A276
• Transport Package: Apply The Shipping Packing
• Specification: 3mm*10mm-30mm*180mm.
• Trademark: CHENGQUAN
• Origin: Hubei, Huangshi
• HS Code: 7228600000
• Production Capacity: 500tons Per Month

Product Description

Similar Grades:
SUS 304
Shape: 
Round, Flat, Square.
Size Range:
3mm*10mm-30mm*180mm.
Steel-making Condition: 
EF, EF/EAF+LF+VD, EF/EAF+ESR
Delivery Condition:
Annealed , Quenched + Tempered

Surface Condition: 
Black, Grinded, Peeled, Rough turned, Polished

Features:
1.Competitive price
2.Immediate delivery
3.Premium quality
4.Reliable service
5.MOQ: 1 Ton
 
 

Packing details	In seaworthy packing, as your requirement.
Delivery details	within 30-50 days

Chemical Composition(%)
 

Steel Grade	C	Si	Mn	P	S	Cr	Ni	N
304	0.08 max	1.00 max	2.0 max	0.045 max	0.030 max	18.0-20.0	8.0-11.0	/
304L	0.03 max	1.00 max	2.0 max	0.045 max	0.030 max	18.0-20.0	8.0-12.0	/
304N	0.08 max	1.00 max	2.0 max	0.045 max	0.030 max	18.0-20.0	8.0-11.0	0.10-0.16

 

Mechanical Properties

Steel Grade	Delivery Condition	Thickness	Tensile Strength (Mpa)	Yield Strength (Mpa)	Elongation in 2 in. (50 mm)	Reduction of Area
304	Annealed	12.7mm max	620 Mpa min	310 Mpa min	30% min	40% min
304	Annealed	12.7mm min	515 Mpa min	205 Mpa min	30% min	40% min
304L	Annealed	12.7mm max	620 Mpa min	310 Mpa min	30% min	40% min
304L	Annealed	12.7mm min	485 Mpa min	170 Mpa min	30% min	40% min
304N	Annealed	Whole Sizes	550 Mpa min	240 Mpa min	30% min	/
304/304L/304N	Relatively severe cold work	19.5mm max	860 Mpa min	690 Mpa min	12% min	35% min
304/304L/304N	Relatively severe cold work	19.5mm - 25.4mm	795 Mpa min	550 Mpa min	15% min	35% min
304/304L/304N	Relatively severe cold work	25.4mm - 31.75mm	690 Mpa min	345 Mpa min	24% min	45% min
304/304L/304N	Strain Hardened	50.8mm max	650 Mpa min	515 Mpa min	25% min	40% min

 

 
 
Applications:
Frame work, braces, supports, plates, marine, food, etc.
 
Introduction:
304 Stainless Steel Flat Bar, is for all applications where greater strength and superior corrosion resistance is required. 304 Stainless Steel Flat Bar has a durable dull, grainy mill finish and is widely used for all types of fabrication projects that are exposed to the elements.
 