DIN 100cr2 1.3501 Cold Working Tool Steel

• Type: Round
• Standard: DIN, BS
• Composition: Ferrous Steel Scrap
• Technique: Hot Forged or Hot Rolled
• Shape: Round,Flat or Square
• Surface Treatment: Black Surface, Grinded,Peeled,Milled,Polished
• Model NO.: 100Cr2 1.3501
• Special Use: Mold Steel
• Application: Tool Steel Bar
• Size Range: Round Bar:Dia12~420mm Flat Bar:2~420 X 30~1500mm
• Smelting Process: Ef, Eaf, ESR
• Delivery Condition: Hot Rolled, Forged, Annealed,Quenched and Tempered
• Surface Condition: Black Surface, Grinded,Peeled,Milled,Polished
• Transport Package: Seaworth Packing
• Specification: Round Bar: Dia12~420mm Flat Bar: 2~420 X 30~1500mm
• Trademark: FUSHUN
• Origin: Huangshi, Hubei
• HS Code: 7228600000
• Production Capacity: 5000tons/Year

Product Description

Introduction:
Low alloyed cold working tool steel.

Applications:
It can be used as structural steel for manufacturing of balls, rollers and needles for bearings up to 10 mm of thickness. This steel grade can be used also as cold working tool steel.

Quality Standard:
DIN 17230-1980 Ball and Roller Bearing Steels
ASTM A29 Standard Specification Steel Bars, Carbon and Alloy, Hot-Wrought, General Requirements

All Grades Comparison:

ASTM	Material No.	EN
50100	1.3501	100Cr2

Chemical Composition(%)

Steel Grade	C	Si	Mn	P	S	Cr	Ni	Cu
100Cr2/1.3501	0.90-1.05	0.15-0.35	0.25-0.45	0.030 max	0.025 max	0.40-0.60	0.30 max	0.30 max
50100	0.98-1.10	0.15-0.35	0.25-0.45	0.030 max	0.025 max	0.40-0.60	0.30 max	0.30 max

HEAT TREATMENT:
· FORGING:forming temperature: 1100-850°C.
· SOFT ANNEALING: Heat to 730-760°C, cool slowly. This will produce a maximum Brinell hardness of 207.
· STRESS RELIEVING: Stress relieving to remove machining stresses should be carried out by heating to approx. 600-650°C, holding for 1-2 hours at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
· HARDENING: Harden from a temperature of 780-810°C, 820-850°C followed by water or oil quenching. Hardness after quenching is about 60 HRC.
· TEMPERING: Tempering temperature: 150-180 °C.

Mill′s test certificate:
EN 10204/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing.